Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was dissolved in de-ionized water. The FT-IR analysis and the XRD study were exhibited that the crystal structure and purity of the ZrO2/ZnO nanocomposite FESEM images was indicated the morphology and the average size of the NPs. The average size of the ZrO2/ZnO nanocomposite was determined 37 nm.